Byk 1006 Fugaflex 10 Kg

Cement and Polymer Based, High Performance, Water Repellent, Silicone Additive, Flexible Joint Filler

Downlod PDF

BYK 1006 FUGAFLEX, Cement and polymer based, flexible, water repellent, silicone added. It is used in the joints of materials such as ceramic, porcelain, granite and marble and is not affected by temperature differences, water and vibration.

In compliance with TS EN 13888 – CG2WA standards.
CG : Cement Based Grouting
2 : Additional Features Improved
W : Reduced Water Absorption
A : High Wear Resistance

Fields of Application

• For indoor and outdoor applications, vertical and horizontal applications,
• Hotel, hospital, shopping center, housing etc.
• In all wet areas,
• In swimming pool and drinking water tank,
• It is used in all kinds of decorative applications.

Advantages

• Mixed only with water.
• Water repellent.
• It is resistant to mold and dirt formation.
• Resistant to impacts, vibrations and detergents.
• Easy to prepare and apply,
• 3-15 mm. Suitable for width-bearing joints,
• Resistant to water and frost,

Technical Features
Structure of the Material
 Special cement, mineral fillings, polymers additive
Density
 1,85 kg/lt
Colour
 White and Colors
Stress Strength
 ≥ 16 N/mm²
Flexural Strength
 ≥ 4 N/mm²
Flexural Strength after freeze
 ≥ 2.5 N/mm²
Water Absorption after 30 min
 ≤ 2 gr
Water Absorption after 4 hours
 ≤ 5 gr
Wear Strength
 <1000 mm3
Application Thickness
 3-15 mm
Application Surface Temperature
 +5ºC / +35ºC
Service Temperature
 -40ºC / +80ºC
Initial Curing Time
 3–5 minutes
Workable Time
 1 hour
Opening the Traffic
 24 hours

The values above are given for +23°C and 50% relative humidity. While higher temperatures shorten the period, lower temperatures extend it

Application Procedure

Preparation of the Substrate

Making strength of adhesive should be expected before starting joint sealant application. 48 hours of waiting time is generally sufficient. The grout in the joints should be cleaned and the joints should be emptied. Joints of highly absorbent materials must be moistened before filling.

Mixing

Clean water as described on the package is put into a clean mixing bowl. When the BYK 1006 FUGAFLEX bag is opened slowly into the water, it is about 3 minutes until it is homogenous with the 400-600-speed mixing drill. Mixed. The material should not remain in the pellet. After resting the material for 3 minutes again 1 min. ready for application by mixing. Different water ratios and different forms of mixing may cause unwanted color differences.

Mixing Ratio

For 20 kg/1 bag of BYK 1006 FUGAFLEX approximately 6,00-6,60 lt of water should be used. For 10 kg/1 bag of BYK 1006 FUGAFLEX approximately 3,00-3,30 lt of water should be used. For 5 kg/1 bag of BYK 1006 FUGAFLEX approximately 1,50-1,65 lt of water should be used.

Application
The mixed material is placed with rubber trowel by making diagonal movements to the joints. In deep joints, the material should first be expected to collapse and then this process should be repeated. In extreme hot weather and on absorbent surfaces, the joint material may suddenly lose water and cause surface cracks. Therefore, the joints must be moistened with a wet sponge before application. When the materials left to dry are pressed against finger pressure, the surfaces are finalized with a wet sponge and the remaining material on the ceramic surface is cleaned.
Consumption

Variable
Consumption Table for Cement Based Grouting (Depth: 8 mm) Values are given in gr / m2.

Ceramic Dimensions
2 mm
3 mm
4 mm
5 mm
6 mm
10x10 550 800 1100 1350 1600
10x20 400 650 850 1050 1250
15x15 450 650 900 1000 1350
15x20 300 500 650 800 1000
20x20 300 450 600 750 900
20x25 275 400 500 700 800
20x30 250 375 500 600 750
30x30 200 300 400 500 600
Package
20 kg – 10kg – 5 kg Kraft bag
Cleaning of Application Tools
Tools and equipments should be clean with water after application.
Watch Points

• In BYK 1006 FUGAFLEX application, suitable temperatures should be expected if ambient and surface temperature are below
+ 5 ° C or above + 35 ° C. It should not be applied in extremely hot, rainy or very windy weather.
• In outdoor applications, for the first 24 hours should be protected from sun, rain, wind and freezing.
• Working and reaction times in grouting mortars are affected by air temperature, humidity and floor temperatures.
• High temperatures accelerate hydration and the working time is shortened accordingly. Low temperatures slow down hydration and thus extend the working time. For the material to be completed, the floor temperature and ambient temperature to be applied must not fall below the minimum permissible temperature.

Shelf Life
Shelf life is 12 months from the date of production when stored properly at +5 oC to +30 oC at room temperature, away from direct sunlight. Opened packages should be consumed within 1 week by closing the mouths
Storage
The product should be stored in its original package, in a cool and dry place protected from frost. For short term storage, maximum 2 palettes should be placed on top of each other and the shipment should be made on a ‘first come, first go’ basis. Palettes should not be placed on top of each other during long term storage.
Health and Safety Precautions
It is dangerous to approach the application sites with fire. Fresh air should be circulated in the storage and the application sites. During the application, a protective apparel, protective gloves, goggles and masks which comply with the Occupational Health and Safety Rules should be used. Due to the irritation effect of the uncured materials, the mixture should not come into contact with skin and eyes; in case of a contact, the affected area should be washed with plenty of water and soap; in case of swallowing, a physician should be consulted immediately. No food or beverages should be brought to the application area. The product should be stored and kept out of reach of children.
Disclaimer
The technical information given in this publication is based on the present state of our best scientific and practical knowledge. BYK Binyapı Co. is only responsible for the quality of the product. BYK Binyapı Co. is not responsible for results that may occur because the product is used other than advised and/or out of instructions regarding the place and the method of use. This technical form is valid only till a new version is implemented and nullifies the old ones.